Evaluation of various steel types for the evolution of hydrogen in KOH - (:unkn) unknown (Editorial Tecnológica de Costa Rica (entidad editora), 2026)
Evaluación de diferentes aceros para la evolución de hidrógeno en KOH
This paper studies the electrochemical behaviour of different types of low-cost commercial steel (A36, 430 and 304) as electrodes to obtain hydrogen. The aim of this work was to understand hydrogen evolution. The studies were conducted by different electrochemistry techniques like chronoamperometry and voltamperometric curves in different concentrations of KOH (5% and 25% m/m). The 304 stainless steel type in a 25% m/m KOH concentration had the best performance, because in these conditions the potential onset of hydrogen release decreased, demonstrating the lowest potential requirement for use as a bipolar plate.
Se estudió el comportamiento electroquímico de los diferentes tipos de aceros comerciales de bajo costo (A36, 430 y 304) como electrodos para la obtención de hidrógeno. El propósito de este trabajo fue estudiar la evolución de hidrógeno, para lo cual se utilizaron técnicas electroquímicas como cronoamperometría y curvas voltamperométricas, en diferentes concentraciones de KOH (5% y 25% m/m). El acero inoxidable 304 en una concentración de 25%m/m tuvo el mejor desempeño, pues en estas condiciones el inicio de liberación de hidrógeno disminuyó y presentó el menor requerimiento de potencial para su uso como placa bipolar.
Keywords: Voltametría; electrólisis; hidrógeno; hidróxido de potasio; acero; acero inoxidable; cronoamperometría; Voltammetry; Electrolysis; Hydrogen; Potassium hydroxide; Steel; Stainless steel; Chronoamperometry