In this study, we analyze the degradation behavior of conventional polymeric solar cells (PSCs) under constant indoor light illumination. A LED lamp with a color temperature of 2700 K, was used for the indoor light illumination conditions. We compare the results obtained with encapsulated and non-encapsulated devices. The performance of the PTB7:PC70BM-based cell showed an initial maximum power conversion efficiency (PCE) of 12.0% under the luminance of 1000 lux and maximum power density (MPP) of 45.7 μW/cm2. The work describes the results of the measurements and analysis of the degradation process, performed by a current density – voltage (J–V) characteristic curve study under LED light. The analyzed performance parameters were PCE, short circuit current density (JSC), open-circuit voltage (VOC) and fill factor (FF). The PCE of encapsulated devices remained above 80% of the initial value after 624 h.En este estudio, nosotros analizamos el comportamiento de degradación de celdas solares poliméricas convencionales (PSCs) bajo iluminación de luz interior constante. Para las condiciones de iluminación de luz interior se utilizó una lampara LED con una temperatura de color de 2700 K. Nosotros comparamos los resultados obtenidos con dispositivos encapsulados y no encapsulados. El desempeño de las celdas basadas en PTB7:PC70BM muestra una eficiencia de conversión de potencia máxima (PCE) inicial de 12.0% bajo la iluminancia de 100 lux y una densidad de potencia máxima de 45.7 μW/cm2. El trabajo describe los resultados de las mediciones y el análisis del proceso de degradación realizado mediante el estudio de la curva característica densidad de corriente – voltaje (J-V) bajo iluminación LED. Los parámetros de desempeño analizados fueron la PCE, la densidad de corriente de corto circuito (JSC), el voltaje de circuito abierto (VOC) y el factor de llenado (FF). La PCE de los dispositivos encapsulados permaneció por arriba del 80% de su valor inicial después de 624 h.