In this work, we report a degradation study of high-efficiency conventional polymer solar cells (PSCs). The high performance of the PM6:Y7-based device is achieved with a power conversion efficiency (PCE) of up to 15.64% in the first measurement. The article describes the results of the measurements and analysis of the degradation process. The electrical parameters during the degradation process were extracted from the current density – voltage characteristics curves (J–V) under light and dark conditions. Were observed the specific parameters of the selected cells: open-circuit voltage (VOC), short circuit current density (JSC), fill factor (FF), PCE, series (RS), and shunt (RSH) resistance values The PCE of the device decreased down to 64% of the initial PCE after 1056 h.En este trabajo, nosotros reportamos un estudio de celdas solares poliméricas (PSCs) convencionales de alta eficiencia. El alto desempeño del dispositivo basado en PM6:Y7 se logró con una eficiencia de conversión de potencia (PCE) de hasta el 15.64 % en la primera medición. El artículo describe los resultados de las mediciones y el análisis del proceso de degradación. Los parámetros eléctricos durante el proceso de degradación fueron extraídos de las curvas características de densidad de corriente-voltaje (J–V) en condiciones de luz y bajo oscuridad. Se observaron los parámetros específicos de las celdas seleccionadas: voltaje de circuito abierto (VOC), densidad de corriente de cortocircuito (JSC), factor de llenado (FF), PCE, serie (RS) y resistencia en paralelo (RSH). La PCE del dispositivo disminuyó hasta el 64% del su PCE inicial después de 1056 h.